Transparent Iron Oxide Pigment
Transparent Iron Oxide Pigment
Transparent Iron Oxide Pigment
Property: When pigment particles disperse in the medium, the diameter is smaller than the half wavelength of the light, then diffraction happens with an effect of transparence. Transparent iron oxide pigment, with particle diameter of nano-meter-level, possesses very good chemical stability for maintaining the chemical structure and crystal form of the iron oxide pigment, and other property such as acid, alkali, solvent, water and oil resistance. Transparent iron oxide red has the heat stability even more than 300℃. Moreover, it has stronger ability of assimilating the ultraviolet, because of which, transparent iron oxide pigment can also improve the ageing-resistance ability of all kinds of high polymer. Transparent iron oxide also has better assimilating and scattering property of the visible light than normal iron oxide pigment, so it has high saturation and tinting strength.
Application: Wood coatings, automobile coatings, plastic coatings, metal coatings, architectural coatings, artists’ color, etc.
Packing: 25kg per bag with pallet, or requested by the customers
Specification for Transparent Iron Oxide Pigments:
Code
TC102
TC202
TC302
Water Based
TC102W
Water Based
TC202W
Water Based
TC302W
Appearance
Yellow
Powder
Red
Powder
Brown
Powder
Yellow
Powder
Red
Powder
Brown
Powder
Color Shade
Similar
Similar
Similar
Similar
Similar
Similar
Tinting
Strength%
≥95
≥95
≥95
≥95
≥95
≥95
105℃ Volatile Matter%
≤3.5
≤3.5
≤3.5
≤3.5
≤3.5
≤3.5
Water Soluble
Matter%
≤0.5
≤0.5
≤0.5
≤0.5
≤0.5
≤0.5
Residue on 325
Mesh%
≤0.1
≤0.1
≤0.1
≤0.1
≤0.1
≤0.1
PH value
3-5
3-5
3-5
6-8
6-8
6-8
Oil absorption
g/100g
35-40
35-40
35-40
35-40
35-40
35-40
Fe2O3 Content%
≥82.0
≥92.0
≥90.0
≥82.0
≥92.0
≥90.0
Oil Resistance
5
5
5
5
5
5
Water resistance
5
5
5
5
5
5
Alkaline
resistance
5
5
5
5
5
5
Acid resistance
5
5
5
5
5
5
Solvent resistance
(alcohol,
methylbenzene)
5
5
5
5
5
5
Conductivity(＜)
400us/cm
600 us/cm
500 us/cm
400 us/cm
600 us/cm
500 us/cm
Similar to
L1916
L2817